Scaffolds of bioglass derived from BG45S5 (45 wt% SiO2, 24.5 wt% CaO, 24.5 wt% Na2O and 6 wt% P2O5) containing 10 wt% niobium were prepared by gelcasting method. The scaffolds presented a 3D porous structure with interconnected and spherical pores (pore size range 100 μm to 500 μm) and high porosity (89%), similar to trabecular architecture of spongy bone. The compressive strength was 0.18 ± 0.03 MPa which is acceptable for bone repair applications. The in vitro biological studies showed cytocompatibility for human osteoblastic cells as well tendency for higher alkaline phosphatase activity. Therefore, the findings here suggest the great potential of the scaffolds for using in bone tissue engineering.

Abstract Electrospinning is a simple and low-cost way to fabricate fibers. Among the various polymers used in electrospinning, polycaprolactone (PCL) stands out due to its excellent biodegradability and biocompatibility. However, PCL has some limitations such as low bioactivity, hydrophobic surface, and long in vivo degradation. Calcium phosphate ceramics have been recognized as an attractive biomaterial. They are bioactive and osteoinductive, and some are even quite biodegradable. Different contents of particles of beta-tricalcium phosphate (β-TCP) were incorporated in polymer matrix to form fibers of PCL/β-TCP composites by electrospinning for possible application in tissue regeneration. The presence of β-TCP particles promoted some changes in the thermal properties of the fibers. The immersion of PCL/β-TCP 8 wt-% fibers in simulated body fluid (SBF) caused the formation of a denser and homogeneous apatite layer on its surface.

Replacement tissues for tissue engineering can be produced by seeding human cells onto scaffolds. In order to guarantee adequate bio-compatibility, porosity and mechanical resistance for promoting cellular growth, proliferation and differentiation within scaffold structures, it is necessary to investigate and improve materials and processing routes. β-tricalcium phosphate can be considered a very suitable bio-ceramic material for bone therapy because of its biocompatibility, osteo-conductivity and neo-vascularization potential. Alumina is commonly used as a sintering additive. In this study, β-TCP and β-TCP/Al2O3 scaffolds were obtained by gel-casting method. The scaffolds showed high porosity (86-88%) and pore sizes ranging from 200 to 500 µm. Even though alumina did not promote improvement in β-TCP/Al2O3 scaffolds in terms of mechanical performance, they showed great cytocompatibility as there was no cytotoxic and genotoxic effect. Therefore, β-TCP and β-TCP/Al2O3 scaffolds are good candidates for application in tissue engineering.

The effects of the heating rate on a TG curve of a sample have been widely discussed in the literature. This paper shows the influence of heating rate (beta) in thermogravimetry results when stoichiometry determinations are studied. For this purpose the compound Sm(CH3SO3)3.2(3-picNO) was considered beta of 2,5; 5; 10; 20 and 40°C min-1 in dynamic air atmosphere were obtained. The results are in agreement with proposed stoichiometry for beta equal to 2,5 and 5°C min-1. However, using a higher beta the same results were not obtained resulting in false stoichiometry determinations.